Chap 20: Magnetic Properties a) Transmission electron micrograph showing the microstructure of the perpendicular magnetic recording medium used in hard-disk drives. b) Magnetic storage hard disks used in laptop (left) and desktop (right) computers. c) Inside of a hard disk drive. d) Laptop computer

Generation of a Magnetic Field -- Vacuum • Created by current through a coil: I B N = total number of turns  = length of each turn (m) I = current (ampere) B = magnetic field (tesla)

Generation of a Magnetic Field -- within a Solid Material • A magnetic field is induced in the material B B = Magnetic field (tesla) inside the material current I • Relative permeability (dimensionless)

Origins of Magnetic Moments • Magnetic moments arise from electron motions and the spins on electrons. magnetic moments electron electron nucleus spin Adapted from Fig. 20.4, Callister & Rethwisch 8e. electron orbital motion electron spin • Net atomic magnetic moment: -- sum of moments from all electrons. • Four types of response...

Types of Magnetism (3) ferromagnetic e.g. Fe3O4, NiFe2O4 (4) ferrimagnetic e.g. ferrite(), Co, Ni, Gd ( cm as large as 106 !) B (tesla) (2) paramagnetic ( e.g., Al, Cr, Mo, Na, Ti, Zr cm ~ 10-4) vacuum ( cm = 0) (1) diamagnetic ( cm ~ -10-5) e.g., Al2O3, Cu, Au, Si, Ag, Zn H (ampere-turns/m) Plot adapted from Fig. 20.6, Callister & Rethwisch 8e. Values and materials from Table 20.2 and discussion in Section 20.4, Callister & Rethwisch 8e.

Magnetic Responses for 4 Types No Applied Applied Magnetic Field (H = 0) Magnetic Field (H) (1) diamagnetic none opposing Adapted from Fig. 20.5(a), Callister & Rethwisch 8e. Adapted from Fig. 20.5(b), Callister & Rethwisch 8e. (2) paramagnetic random aligned Adapted from Fig. 20.7, Callister & Rethwisch 8e. (3) ferromagnetic (4) ferrimagnetic aligned

Influence of Temperature on Magnetic Behavior With increasing temperature, the saturation magnetization diminishes gradually and then abruptly drops to zero at Curie Temperature, Tc.

Magnetic Domains

Domains in Ferromagnetic & Ferrimagnetic Materials • As the applied field (H) increases the magnetic domains change shape and size by movement of domain boundaries. B sat H H H Adapted from Fig. 20.13, Callister & Rethwisch 8e. (Fig. 20.13 adapted from O.H. Wyatt and D. Dew-Hughes, Metals, Ceramics, and Polymers, Cambridge University Press, 1974.) • “Domains” with aligned magnetic moment grow at expense of poorly aligned ones! induction (B) H Magnetic H H = 0 Applied Magnetic Field (H)

Hysteresis and Permanent Magnetization • The magnetic hysteresis phenomenon B Stage 2. Apply H, align domains Stage 3. Remove H, alignment remains! => permanent magnet! Stage 4. Coercivity, HC Negative H needed to demagnitize! Adapted from Fig. 20.14, Callister & Rethwisch 8e. H Stage 5. Apply -H, align domains Stage 1. Initial (unmagnetized state) Stage 6. Close the hysteresis loop

Magnetic Anisotropy Easy magnetization direction: Ni- [111], Fe- [100], Co- [0001]. Hard magnetization direction: Ni- [100], Fe- [111], Co-

Hard and Soft Magnetic Materials Hard magnetic materials: -- large coercivities -- used for permanent magnets -- add particles/voids to inhibit domain wall motion -- example: tungsten steel -- Hc = 5900 amp-turn/m) B Hard Soft H Soft magnetic materials: -- small coercivities -- used for electric motors -- example: commercial iron 99.95 Fe Adapted from Fig. 20.19, Callister & Rethwisch 8e. (Fig. 20.19 from K.M. Ralls, T.H. Courtney, and J. Wulff, Introduction to Materials Science and Engineering, John Wiley and Sons, Inc., 1976.) 12 12

Iron-Silicon Alloy (97 wt% Fe – 3 wt% Si) in Transformer Cores Transformer cores require soft magnetic materials, which are easily magnetized and de-magnetized, and have high electrical resistivity. Energy losses in transformers could be minimized if their cores were fabricated such that the easy magnetization direction is parallel to the direction of the applied magnetic field.

Magnetic Storage • Digitized data in the form of electrical signals are transferred to and recorded digitally on a magnetic medium (tape or disk) • This transference is accomplished by a recording system that consists of a read/write head -- “write” or record data by applying a magnetic field that aligns domains in small regions of the recording medium -- “read” or retrieve data from medium by sensing changes in magnetization Fig. 20.23, Callister & Rethwisch 8e. http://www.ehow.com/how-does_4968711_solid-state-hard-drives-work.html

Magnetic Storage Media Types • Hard disk drives (granular/perpendicular media): -- CoCr alloy grains (darker regions) separated by oxide grain boundary segregant layer (lighter regions) -- Magnetization direction of each grain is perpendicular to plane of disk Fig. 20.25, Callister & Rethwisch 8e. (Fig. 20.25 from Seagate Recording Media) 80 nm • Recording tape (particulate media): Fig. 20.24, Callister & Rethwisch 8e. (Fig. 20.24 courtesy Fuji Film Inc., Recording Media Division) ~ 500 nm -- Acicular (needle-shaped) ferromagnetic metal alloy particles -- Tabular (plate-shaped) ferrimagnetic barium-ferrite particles ~ 500 nm

Superconductivity Found in 26 metals and hundreds of alloys & compounds Mercury Copper (normal) Fig. 20.26, Callister & Rethwisch 8e. 4.2 K TC = critical temperature = temperature below which material is superconductive

Critical Properties of Superconductive Materials TC = critical temperature - if T > TC not superconducting JC = critical current density - if J > JC not superconducting HC = critical magnetic field - if H > HC not superconducting Fig. 20.27, Callister & Rethwisch 8e.

Meissner Effect Superconductors expel magnetic fields This is why a superconductor will float above a magnet normal superconductor Fig. 20.28, Callister & Rethwisch 8e.

Advances in Superconductivity Research in superconductive materials was stagnant for many years. Everyone assumed TC,max was about 23 K Many theories said it was impossible to increase TC beyond this value 1987- new materials were discovered with TC > 30 K ceramics of form Ba1-x Kx BiO3-y Started enormous race Y Ba2Cu3O7-x TC = 90 K Tl2Ba2Ca2Cu3Ox TC = 122 K difficult to make since oxidation state is very important The major problem is that these ceramic materials are inherently brittle. Suddenly everyone was doing superconductivity. Everyone was doing similar work, making discoveries, & rushing to publish so they could claim to have done it first. Practically, daily new high temp. records were set.

Summary • A magnetic field is produced when a current flows through a wire coil. • Magnetic induction (B): -- an internal magnetic field is induced in a material that is situated within an external magnetic field (H). -- magnetic moments result from electron interactions with the applied magnetic field • Types of material responses to magnetic fields are: -- ferrimagnetic and ferromagnetic (large magnetic susceptibilities) -- paramagnetic (small and positive magnetic susceptibilities) -- diamagnetic (small and negative magnetic susceptibilities) • Types of ferrimagnetic and ferromagnetic materials: -- Hard: large coercivities -- Soft: small coercivities • Magnetic storage media: -- particulate barium-ferrite in polymeric film (tape) -- thin film Co-Cr alloy (hard drive)