Manufacture of Wood-Pottery Composite Board Andi Hermawan, Takeshi Ohuchi, Noboru Fujimoto, Yasuhide Murase Kyushu University-Japan.

Slides:

Advertisements

Similar presentations

Introduction to Woods 1 Close up of Vessel & Cell.

Advertisements

The hot pressing process of oriented strand board: Dr. Azzeddine OUDJEHANE Review of the modeling.

Lecture 2 SANDWICH COMPOSITES

Composite Panel Products for Stage Scenery 2005 USITT Conference & Stage Expo, Toronto, CA March 16-19, 2005 John F. Hunt, P.E. Research Mechanical Engineer.

Strength Performance of Glulam made of Obi-sugi Laminae with low Young’s Modulus of Bending Miyazaki Prefectural Wood Utilization Research Center Akihiro.

Manufacturing Technology

Mechanical Properties MAJOR PROPERTIES: 1.Strength 2.Stiffness Defects are not controllable in large sized pieces Full sized members are not homogenous.

USING Acacia mangium AS A SINGLE RAW MATERIAL IN PRODUCING PARTICLEBOARD Presented by VICTOR PALLICKAL XAVIER.

Effects of APP on the Fire-retardant and Mechanical properties of Wood-flour/HDPE Composite WANG Qing-Wen, SHAO Bo, ZHANG Zhi-Jun, SONG Yong-Ming Northeast.

Casing Spacers & End Seals

Engineering Properties of Wood

Forestry Chapter 8: Wood and Water

1 Sara Pourabbasi IUFRO Division 5 Conference Forest Products IRG/Wood Protection.

Wood pellets combustion with rich and diluted air in HTAC furnace Author: Ramona DINU.

Chapter 16 Processes Used to Form WoodMaterials. Objectives Two basic wood forming processes: bonding and bending. Composition boards: hardboard, insulation.

Materials Part 1: Properties of wood and metals

Experimental Methodology The test setup is illustrated in Figure 3. This setup is often referred to as ‘pitch-catch’ where a piezoelectric transmitter.

1 COMPOSITE MATERIALS What are composite materials? Two or more materials bound together Example from civil engineering: Concrete reinforced with steel.

Packaging considerations in supply chain Traditionally we are using corrugated boxes of various sizes in supply of parts from vendors to automobile manufacturer.

Chapter 29 Determining Simple Beams. 2 Links for Chapter 29 Loads & Supports Properties of Lumber Beam Design Related Web Sites.

SOME PUBLISHED AND UNPUBLISHED ULTRASONIC RESEARCH ON WOOD Frank Beall University of California, Berkeley.

ItemUncoatedEpoxy CoatedPainted GFRP Thread Bar Specimen PT1PT2PT3PTE1PTE2PTE3PTP1PTP2PTP3 Growth Height (cm) Growth.

CE 241 MATERIALS SCIENCE Introduction

Physical and Chemical Properties. Physical and Chemical Changes Explain – Content Connections.

ADVANCED HIGH DENSITY INTERCONNECT MATERIALS AND TECHNIQUES DIVYA CHALLA.

Ch students per table 2.Workbook & Textbook 3.Pencil / Pen 4.Start when quiet.

Introduction to Fibers I. What is a fiber? Fine Fine Flexible Flexible High Aspect Ratio (length-to-width ratio) High Aspect Ratio (length-to-width ratio)

Testing Methods for Composites

Carbon-Carbon Compoistes What are carbon-carbon composites? Carbon - Carbon composites have carbon fibers in carbon matrix.

Fabric Development, Inc.

For. 485: Lignocellulosic Composite Materials Lecture 1-5-2: Consolidation Behavior of Lignocellulosics in Thermal Processes, Part II.

MECHANICAL PROPERTIES OF CERAMICS AND ITS APPLICATION.

Structural Elements.

Sports Medicine: Physical Fitness. 1. Define new terminology 2. Create a fitness profile 3. Set goals for future fitness plans.

Created by: Michael Oyebode

Wood MSE 220 Spring, Strength of wood increases as it dries. A board in the green condition weighs 11.2 lbs, and in the dry condition weighs.

Wood Structure Hardwood Softwood.

Fabrication Method and Characteristics of Fibers

Forest Products Research and Development Centre

PVC CHIP BOARD ACHAL MARKETING Door No.2-92/3, Belve Post & Village, Kundapura

Sierra Assembly Technology Inc.

MATERIALS & THEIR PROPERTIES

Chapter 17 Landfill Liners and Geosynthetics

REPAIR OF TIMBER BEAMS USING CFRP SHEETS

MASS-PRODUCTION OF SYNTHETIC SLEEPER

Preparation and Mechanical Evaluation of Graphene & Silicon Carbide Wood Ceramic Composite School of Forest Sciences Cao Rulong China

Introduction Methods Results Conclusions

Date of download: 10/23/2017 Copyright © ASME. All rights reserved.

Lecturer: Dr. Frederick Owusu-Nimo

Prediction of the Flexural Modulus of Fibre Reinforced Thermoplastics as used for Kayak Paddle Blades. P.D. EWART* AND CJR VERBEEK The Department of Materials.

Lecture #19 Structure of Wood.

EML 4230 Introduction to Composite Materials

Engineered Composite Building Products

Ceramic Matrix Composites

Carbon-Carbon Compoistes

Metal Matrix Composites

Engineered Building Products

Warm Up # What are some physical properties that are used to evaluate materials?

Example of Wood Oak Maple Birch Nice to meet you. Our theme is wood.

چوب پلاستیک و کاربرد های آن.

Ашық сабақ 7 сынып Файлдар мен қапшықтар Сабақтың тақырыбы:

Windows басқару элементтері

Zeinab A. Osman, Ph.D Department of Cellulose Chemistry and Technology

UNIT 3 REVIEW MATERIAL.

Қош келдіңіздер!.

Forces and Materials.

Информатика пән мұғалімі : Аитова Карима.

Presentation transcript:

Manufacture of Wood-Pottery Composite Board Andi Hermawan, Takeshi Ohuchi, Noboru Fujimoto, Yasuhide Murase Kyushu University-Japan

Introduction Board evaluation Effectiveutilization Wood-Pottery Composite Board Prune wood Pottery stone scrap Three-layer composite board Single-layer composite board

Evaluation of Board Properties Physical and mechanical properties (JIS A 5908):Physical and mechanical properties (JIS A 5908): Density, moisture content, bending test, internal bond test, thickness swelling test Incombustible properties (JIS A 1322):Incombustible properties (JIS A 1322): After flaming time, glowing time, carbonization length, weight loss Board after test Schematic diagram of incombustible properties test Meker burner Specimen Window

Properties of Wood- Pottery Composite Board The board (three-layer) has excellent internal bond strength, thickness swelling and incombustible propertiesThe board (three-layer) has excellent internal bond strength, thickness swelling and incombustible properties Bending strength of the board was poorBending strength of the board was poor Therefore, improvement of bending properties of the board is necessary