© Corrosion Properties Of HVOF-Coated Steel In Simulated Concrete Pore Electrolyte And Concentrated Chloride Environments Khaled, MM; Yibas, BS ELSEVIER SCIENCE SA, SURFACE COATINGS TECHNOLOGY; pp: ; Vol: 202 King Fahd University of Petroleum & Minerals Summary The corrosion susceptibility of steel and HVOF-coated steel in solutions simulating the alkaline concrete pore environment and with the addition of chloride was investigated using potentiodynamic polarization and potential step techniques. The surface characterization was performed using SEM and the surface elemental analysis was determined by EDS. The concentration of chloride was 2.8 M to simulate the concentration of chloride spread in many local regions of Saudi Arabia and called Sabkha. It was found that, in the case of the simulated concrete pore electrolytes, the HVOF coating resulted in an anodic shift of the corrosion potential with marginal effect on the corrosion current. However, upon addition of 2.8 M chloride solution, the corrosion rate of the HVOF-coated steel was found to increase by a factor of two. SEM showed a network of pores within the coating which provides a path for the electrolyte. This would result in preferential corrosion around splat boundaries and confirmed by EDS which showed that the corroded splats have higher oxide contents. Potential step experiments at 400 mV above open circuit potential showed a suppressed current of the HVOF-coated steel compared to the steel substrate alone. The corrosion potential versus time experiments resulted in a more anodic Ecorr which decreased with time and became equal to the Ecorr of the bare steel after 34 h. After that, the corrosion potential of the HVOF-coated steel decreased due to the increase in galvanic coupling between the steel and the HVOF coating. (c) 2007 Elsevier B.V. All rights reserved. Copyright: King Fahd University of Petroleum & Minerals;
© References: ASHARY AA, 1991, SURF COAT TECH, V49, P78 CHERIGUI M, 2005, SURF COAT TECH, V192, P19, DOI /j.surfcoat DWYLER AL, 1995, ADV THERMAL SPRAY SC, P615 ERNING U, 1999, P UN THERM SPRAY C, P462 FEDRIZZI L, 1998, P EUR 98 C EFC UTREC FEDRIZZI L, 2002, WEAR, V253, P1173 FEDRIZZI L, 2004, ELECTROCHIM ACTA, V49, P2803, DOI /j.electacta GUILEMANY JM, 2002, SURF COAT TECH, V153, P107 GUILEMANY JM, 2006, CORROS SCI, V48, P2998, DOI /j.corsci HARVEY D, 1995, P INT THERM SPRAYING, P531 HARVEY D, 2000, THERMAL SPRAY SURFAC, P991 HEARLEY JA, 2000, SURF COAT TECH, V123, P210 HODGKIESS T, 1998, P 15 INT THERM SPRAY, P63 JOSHI SV, 1991, SURF COAT TECH, V50, P67 KAWAKITA J, 2005, CORROS SCI, V47, P2053, DOI /j.corsci KO PL, 2002, WEAR, V252, P880 KULKARNI A, 2004, MAT SCI ENG A-STRUCT, V369, P124, DOI /j.msea MARPLE BR, 1989, P UN THERM SPRAY C, P122 MARPLE BR, 2001, J MATER PROCESS TECH, V117, P418 MATTHEWS S, 2003, ACTA MATER, V51, P4267, DOI /S (03) NAGY Z, 1993, MOD ASPECT ELECTROC, V25, P135 NORMAND B, 1998, MATER SCI FORUM, V607, P289 NORMAND B, 1998, P 15 INT THERM SPRAY, P69 RABIEI A, 1999, MAT SCI ENG A-STRUCT, V269, P152 ROSSI S, 2000, MATER CORROS, V51, P552 SAHRAOUI T, 2004, MATER LETT, V58, P654, DOI /j.matlet SAVARIMUTHU AC, 2000, P 1 INT THERM SPRAY, P1095 SAVARIMUTHU AC, 2001, J THERM SPRAY TECHN, V10, P502 SCHORR BS, 1999, MATER CHARACT, V42, P93 SIDHU TS, 2006, ACTA MATER, V54, P773, DOI /j.actamat SIITONEN P, 1992, P INT THERM SPRAY C, P SIITONEN P, 1994, P 7 NAT THERM SPRAY, P SOBOLEV VV, 1994, MATER LETT, V18, P SUEGAMA PH, 2002, J APPL ELECTROCHEM, V32, P TURUNEN E, 2006, MAT SCI ENG A-STRUCT, V415, P1, DOI /j.msea Copyright: King Fahd University of Petroleum & Minerals;
© WANG Y, 2004, SURF COAT TECH, V183, P18, DOI /j.surfcoat For pre-prints please write to: Copyright: King Fahd University of Petroleum & Minerals;