Welding Design 1998/MJ1/MatJoin2/1 Design. Lesson Objectives When you finish this lesson you will understand: Mechanical and Physical Properties (structure.

Slides:



Advertisements
Similar presentations
Mechanical Properties of Metals
Advertisements

Chapter 3 Mechanical Testing
Dr. HABEEB HATTAB HABEEB Office: BN-Block, Level-3, Room Ext. No.: 7292 Lecturer: Dr. HABEEB ALANI.
CREEP  It can be defined as the slow & progressive (increasingly continuing) deformation of a material with time under a constant stress.  It is both.
Material testing Lesson 2.
Grain Boundaries Ni-Base Superalloy Waspalloy 50µm high-angle grain boundary (  >15°) low-angle grain boundary.
MECHANICAL PROPERTIES
Professor Joe Greene CSU, CHICO
Chapter 11 Mechanical Properties of Materials
MECHANICAL PROPERTIES OF MATERIALS
NOTCH EFFECTS INTRODUCTION OF A NOTCH AFFECTS THE FRACTURE PROCESS Eg: INCREASES THE DUCTILE-BRITTLE TRANSITION TEMPERATURE OF STEEL NOTCH CREATES A LOCAL.
Engineering materials lecture #14
Materials Engineering – Day 2
ME 388 – Applied Instrumentation Laboratory Fatigue Lab.
NAVAL MATERIALS.
EXPERIMENT # 3 Instructor: M.Yaqub
Welding Metallurgy 1998/MJ1/MatJoin3/1 Welding Metallurgy.
Jiangyu Li, University of Washington Lecture 18 Impact Test and Stress Concentration Mechanical Behavior of Materials Section 4.8, 8.1, 8.2 Jiangyu Li.
Tensile Test The most common static test is the uniaxial tensile test, which provides information about a variety of properties. As a load is applied to.
Mechanical Properties of
Lecture 26: Mechanical Properties I: Metals & Ceramics
ENGR 225 Section
LECTURER 3 Fundamental Mechanical Properties (i)Tensile strength
LECTURER6 Factors Affecting Mechanical Properties
Mechanical Properties Testing
Design 2.
Mechanical Properties
Class #1.2 Civil Engineering Materials – CIVE 2110
Unit V Lecturer11 LECTURE-I  Introduction  Some important definitions  Stress-strain relation for different engineering materials.
Mechanical Properties of Materials
FATIGUE Fatigue of Materials (Cambridge Solid State Science Series) S. Suresh Cambridge University Press, Cambridge (1998)
1 Class #2.1 Civil Engineering Materials – CIVE 2110 Strength of Materials Mechanical Properties of Ductile Materials Fall 2010 Dr. Gupta Dr. Pickett.
Mechanical Behavior, Testing and Manufacturing Properties of Materials
MECHANICAL TESTING.
Welding Inspection and Metallurgy
Jiangyu Li, University of Washington Yielding and Failure Criteria Plasticity Fracture Fatigue Jiangyu Li University of Washington Mechanics of Materials.
Chapter 2 Properties of Metals.
Mechanical Properties of Materials
PHF110: Basic Physics and Materials Dr Mark A. E. Jepson Room: S227
Properties of Materials "those characteristics that help identify and distinguish one material from another” (p. 140) Page numbers are in reference to:
Haseeb Ullah Khan Jatoi Department of Chemical Engineering UET Lahore.
Group 2 presentation Q : stress and strain curve presentation.
STRUCTURES Young’s Modulus. Tests There are 4 tests that you can do to a material There are 4 tests that you can do to a material 1 tensile This is where.
Mechanical properties of dental biomaterials 2
Physical properties Enrollment numbers Government engineering collage,Palanpur sub:- Applied.
SIMPLE STRESS & STRAIN ► EN NO GUIDED BY EN NO PROF. V.R.SHARMA GEC PALANPUR APPLIED MECHANICS DEPARTMENT.
Materials Science Chapter 8 Deformation and Fracture.
PROPERTIES OF MATERIALS ENF 150 Chapter 10: Properties of Materials.
DEPARTMENT OF MECHANICAL AND MANUFACTURING ENGINEERING
CHAPTER 4 : MECHANICAL PROPERTIES OF METALS
Material Testing under Tension
Mechanical Properties
Tests For Materials.
Introduction We select materials for many components and applications by matching the properties of the material to the service condition required of the.
Methods to Maximize Design Life
LECTURER 3 Fundamental Mechanical Properties (i)Tensile strength
Mechanical Properties of Metals
Mechanical Properties: Part One
Chapter 3 Mechanical Properties of Materials
Poisons Ratio Poisons ratio = . w0 w Usually poisons ratio ranges from
Mechanics of Materials Lab
1/18/2019 6:28 AM C h a p t e r 8 Failure Dr. Mohammad Abuhaiba, PE.
LECTURE-I Introduction Some important definitions
Mechanical Properties: 1
Mechanical Properties of Metals
Elastic & Plastic behavior of Materials
PDT 153 Materials Structure And Properties
Mechanical Properties Of Metals - I
Tutorial.
Mechanical Property 기계적 성질
Presentation transcript:

Welding Design 1998/MJ1/MatJoin2/1 Design

Lesson Objectives When you finish this lesson you will understand: Mechanical and Physical Properties (structure sensitive and structure insensitive) Learning Activities 1.Read Handbook pp View Slides; 3.Read Notes, 4.Listen to lecture 5.Do on-line workbook 6.Do homework Keywords Structure Sensitive Properties, Structure Insensitive Properties, Stress, Strain, Elastic Modulus, Yield Strength, Tensile Strength, Ductility, Elongation, Proportional Limit, Fatigue, Stress Range, Stress Ratio, Endurance Limit, Toughness, Charpy, Ductile, Brittle, Hardness, Creep Design

Welding Design 1998/MJ1/MatJoin2/3 Welding Design l Welding design involves consideration of strength requirements, cost, and service conditions Mechanical & Physical properties Joint Design Welding stress and distortion Introduction T

Welding Design 1998/MJ1/MatJoin2/4

Welding Design 1998/MJ1/MatJoin2/5 Mechanical Properties

Welding Design 1998/MJ1/MatJoin2/6 Stress and Strain l Stress is defined as force per unit area Pounds per square inch, psi Megapascals (Newtons/mm 2 ), MPa l Strain is defined as change in dimension divided by original dimension Expressed as percent (%) Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/7 Tensile Test l Tensile test provides a plot of stress versus strain Elastic Modulus (E) Yield strength Tensile Strength Ductility Strain Stress, psi or MPa Yield Strength Tensile Strength Slope = Modulus Ductility Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/8 A = Proportional (Elastic) Limit B = 0.2% Offset Yield Strength C = Ultimate Tensile Strength Slope = Elastic Modulus

Welding Design 1998/MJ1/MatJoin2/9

Turn to the person sitting next to you and discuss (1 min.): The elastic portion of the stress- strain curves for steel, rubber, aluminum and tungsten are plotted here. Which material is which?

Welding Design 1998/MJ1/MatJoin2/11 Fatigue l Fatigue is material failure due to cyclic loading l Cyclic rather than static loading Tension - compression Tension - tension l Occurs at stress levels below the tensile strength Tension - Tension Tension - Compression Stress 0 Fatigue Design

Welding Design 1998/MJ1/MatJoin2/12 Linnert, Welding Metallurgy AWS, 1994 Stress Range Stress Ratio

Welding Design 1998/MJ1/MatJoin2/13 Linnert, Welding Metallurgy AWS, 1994

Welding Design 1998/MJ1/MatJoin2/14 Fatigue Appearance l Distinct fracture surface has a characteristic texture Concentric line pattern Smooth portion referred to as clamshell texture l Sources of fatigue Cracks Notches Sharp corners Initiation site Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/15 Linnert, Welding Metallurgy AWS, 1994 Endurance Limit

Welding Design 1998/MJ1/MatJoin2/16 Factors Affecting Fatigue l Welds have pre-existing stress risers or initiation sites from which fatigue cracks can grow Slag intrusions Undercut Weld toe radius l Other factors Butt joints vs. lap joints Sharp corners, notches UndercutIntrusion Smooth weld toe Fatigue Design

Welding Design 1998/MJ1/MatJoin2/17 Fatigue of Welds l In general, welds have pre-existing stress risers or initiation sites from which fatigue cracks can grow Slag intrusions Undercut Hardness variations l Design considerations Butt joints rather than lap joints Lap joint Butt joint UndercutIntrusion Mechanical Properties T

Turn to the person sitting next to you and discuss (1 min.): In the previous discussion we looked at stress cycles where both the min. and max. stress were positive. What do you think might happen if the minimum stress were compressive like the bottom curve?

Turn to the person sitting next to you and discuss (1 min.): In the previous discussion we looked at stress cycles where both the min. and max. stress were positive. What do you think might happen if the minimum stress were compressive like the bottom curve? Goodman Diagram

Welding Design 1998/MJ1/MatJoin2/20 Toughness Ability of a metal to resist fracture in the presence of a notch, and to accommodate loads by plastic deformation Rate of Straining Nature of Load - Uniaxial or Multiaxial Temperature Conditions Influencing Behavior

Welding Design 1998/MJ1/MatJoin2/21 Toughness l Toughness is a measure of the ability of a material to absorb energy prior to failure l Impact energy measured by the Charpy test Scale Hammer Specimen Charpy V-Notch specimen Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/22 Ductile to Brittle Transition l Steels have greatly reduced toughness at lower temperatures Temperature Energy absorbed for fracture Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/23 Linnert, Welding Metallurgy AWS, 1994

Welding Design 1998/MJ1/MatJoin2/24

Welding Design 1998/MJ1/MatJoin2/25 Linnert, Welding Metallurgy AWS, 1994

Welding Design 1998/MJ1/MatJoin2/26 Effect of Discontinuities on Properties l Fracture mechanics - analysis of the failure of structural materials with pre-existing flaws l Fracture toughness testing is used for brittle materials or thick sections Strain rate Temperature Thickness Mechanical Properties T

Turn to the person sitting next to you and discuss (1 min.): Consider the two beams. Which will experience less impact stress?

Turn to the person sitting next to you and discuss (1 min.): Consider the two beams. Which will experience less impact stress? (1)For a steady load, doubling the length of the beam will double the resulting bending stress (2)For an impact load, doubling the length of the beam will reduce the resulting impact stress to 70.7% of the original. See “Design of Weldments” p Lincoln Arc Welding Foundation

Welding Design 1998/MJ1/MatJoin2/29 Hardness l Hardness - resistance to indentation l Measured by pushing an indenter into the surface of a material l Wear resistant materials have high hardness l Hardness can be correlated to tensile strength Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/30 Measures of Ductility l % Elongation at failure l % Reduction in area Mechanical Properties T

Welding Design 1998/MJ1/MatJoin2/31 Linnert, Welding Metallurgy AWS, 1994

Welding Design 1998/MJ1/MatJoin2/32

Welding Design 1998/MJ1/MatJoin2/33