ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 1 ENT 353 ADVANCED MECHANICAL DESIGN Lecture 2. Fatigue of Metals 16/07/2007.

Slides:

Advertisements

Similar presentations

Kjell Simonsson 1 Low Cycle Fatigue (LCF) analysis (last updated )

Advertisements

FRACTURE, FAILURE AND FATIGUE Catastrophic failure in materials resulting from crack development.

ME 240: Introduction to Engineering Materials Chapter 8. Failure 8.1 CHAPTER 8.

CREEP  It can be defined as the slow & progressive (increasingly continuing) deformation of a material with time under a constant stress.  It is both.

Kjell Simonsson 1 High Cycle Fatigue (HCF) analysis (last updated )

Design of Machine Elements

CTU in Prague, Faculty of Mechanical Engineering DAF Page 1 Concentration factors Shape Factor or Stress Concentration Factor of an Elastic Stress Relative.

CHAPTER 7 Fatigue Failure Resulting from Variable Loading

Fatigue Failure Resulting from Variable Loading

Design of Machine Elements

Over the Next Several Days

DESIGNING AGAINST FATIGUE

Kjell Simonsson 1 Introduction to Lecture 1 TMMI09, autumn 2011 (last updated )

FATIGUE TEST EXPERIMENT # 5 Instructor: M.Yaqub. FATIGUE.

Failure Theories Why do parts fail? What kind of stresses?

Lecture #19 Failure & Fracture

Three Stages of Fatigue Failure

LECTURE # 39. FATIGUE LOADING OF TENSION JOINTS Table 8-16 lists average fatigue stress- concentration factors for the fillet under the bolt head and.

Chapter 5 – Design for Different Types of Loading

Chapter 6 Fatigue Failure Theories

© 2011 Autodesk Freely licensed for use by educational institutions. Reuse and changes require a note indicating that content has been modified from the.

Static and Fatigue Bolt Design

Design Agains Fatigue - part Fatigue Endurance Prediction Design Agains Fatigue - part Fatigue Endurance Prediction Milan Růžička

Chapter 2 Stress and Strain -- Axial Loading

Chapter 7 Fatigue Failure Resulting from Variable Loading

Chapter 7 Fatigue Failure Resulting from Variable Loading

Screws, Fasteners, and the Design of Nonpermanent Joints

FRACTURE MECHANICS AND FATIGUE DESIGN HANS MF PANJAITAN Marinteknisk Senter Otto Nielsens Veg Trondheim Norway Mobile:

DESIGN FOR FATIGUE STRENGTH

Welding Design 1998/MJ1/MatJoin2/1 Design. Lesson Objectives When you finish this lesson you will understand: Mechanical and Physical Properties (structure.

1 Jiangyu Li, University of Washington Lecture 18 Fatigue Mechanical Behavior of Materials Sec Jiangyu Li University of Washington Mechanics of.

Chapter 7 Fatigue Failure Resulting from Variable Loading

Mechanics of Materials Lab

FATIGUE Fatigue of Materials (Cambridge Solid State Science Series) S. Suresh Cambridge University Press, Cambridge (1998)

1 Class #2.1 Civil Engineering Materials – CIVE 2110 Strength of Materials Mechanical Properties of Ductile Materials Fall 2010 Dr. Gupta Dr. Pickett.

Fatigue Failure Due to Variable Loading

1 Design for Different Type of Loading Lecture Notes Dr. Rakhmad Arief Siregar Kolej Universiti Kejuruteraan Utara Malaysia Machine Element in Mechanical.

Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.

FATIGUE Fatigue of Materials (Cambridge Solid State Science Series) S. Suresh Cambridge University Press, Cambridge (1998) MATERIALS SCIENCE &ENGINEERING.

MECHANICAL TESTING.

Chapter 7 Fatigue Failure Resulting from Variable Loading

MECH 401 Mechanical Design Applications Dr. M. O’Malley– Master Notes

1 INTRODUCTION TO DESIGN SKMM 1512 Semester 2 Session 2014/2015.

Jiangyu Li, University of Washington Yielding and Failure Criteria Plasticity Fracture Fatigue Jiangyu Li University of Washington Mechanics of Materials.

Course No.: MEBF ZC342 MACHINE DESIGN

STRUCTURES Young’s Modulus. Tests There are 4 tests that you can do to a material There are 4 tests that you can do to a material 1 tensile This is where.

Lecture 17 introducing FATIGUE FAILURE Atta ul Haq GIK Institute-Fall

IS:800 Section 13 FATIGUE. Introduction Mechanism of Fatigue Fracture Factors Affecting Fatigue Strength Design Strength & Cumulative Fatigue Damage IS:800.

EUROnu WP2 meeting, Cracow 14 October 20101/32M.Kozień & B.Szybiński NEXT STEPS IN STRENGTH ANALYSIS OF THE HORN EUROnu Project Cracow University of Technology.

FATIGUE TESTING Presented by- BIPIN KUMAR MISHRA 2011EME11 SHEELOO SINGH 2011EME08.

Mechanical Properties of Materials MMM 220

Tests For Materials.

FLUCTUATING STRESSES SUBJECT: Design of machine elements

Machine Design: An Overview

Dr. S & S.S.GHANDHY GOVERNMENT ENGINEERING COLLEGE

Introduction We select materials for many components and applications by matching the properties of the material to the service condition required of the.

C. K. Pithawala College of Engineering and Technology

Methods to Maximize Design Life

LECTURER 3 Fundamental Mechanical Properties (i)Tensile strength

Mechanical Properties of Metals

Mechanics of Materials Lab

Mechanics of Materials Lab

MATERIALS TESTING LECTURE-10

Tutorial in Mechanical Properties

EML 2023 – Stress Analysis Lecture 1 – Stress State.

1/18/2019 6:28 AM C h a p t e r 8 Failure Dr. Mohammad Abuhaiba, PE.

Fatigue failure of materials

Lab8: Fatigue Testing Machine

Lab8: Fatigue Testing Machine

Mechanical Failure(파괴)

Presentation transcript:

ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 1 ENT 353 ADVANCED MECHANICAL DESIGN Lecture 2. Fatigue of Metals 16/07/2007

ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 2 Objectives To considered the analysis and design of parts subjected to variable loading. To describe how parts fail under variable loading and how to portion them to successfully resist such condition.

ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 3 Variable Loading  Introduction to Fatigue in Metals Introduction to Fatigue in Metals  Strain-Life Relationships Strain-Life Relationships  Stress-Life Relationships Stress-Life Relationships  The endurance Limit The endurance Limit  Fatigue Strength  Endurance-Limit Modifying Factors Endurance-Limit Modifying Factors  Stress Concentration and Notch Sensitivity  Fluctuating Stresses Fluctuating Stresses  Failure Loci under Variable stresses Failure Loci under Variable stresses  Cumulative fatigue Damage Cumulative fatigue Damage  The Fracture-Mechanics Approach

ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 4 Variable Loading  Static conditions => the specimen is tested to destruction, and so the stresses are applied only once. In most testing of those materials that relate to the stress- strain diagram. Static conditions

ENT 353 Advanced Mechanical Design Dr. Haftirman /Shah Fenner Khan/Ahmad Yusri 5 Variable Loading  Variable loading=> repeated, alternating, or fluctuating stresses