Microstructure of the different Ti-6Al-4V Aida Amroussia, PhD Candidate 1 Pr. Carl J Boehlert 1 Dr. Frederique Pellemoine 2 Pr. Wolfgang Mittig 2 1 Michigan.

Similar presentations


Presentation on theme: "Microstructure of the different Ti-6Al-4V Aida Amroussia, PhD Candidate 1 Pr. Carl J Boehlert 1 Dr. Frederique Pellemoine 2 Pr. Wolfgang Mittig 2 1 Michigan."— Presentation transcript:

1 Microstructure of the different Ti-6Al-4V Aida Amroussia, PhD Candidate 1 Pr. Carl J Boehlert 1 Dr. Frederique Pellemoine 2 Pr. Wolfgang Mittig 2 1 Michigan State University 2 Facility For Rare Isotope Beams 1

2 Microstructure of the powder metallurgy rolled Ti-6Al-4V 20 µm

3 Microstructure of the as received DMLS Ti-6Al-4V Cross section Top view 20µm

4 Microstructure DMLS-HT1: Heat treatment 850 C for 2 h (~8 C /min) then furnace cooling Cross section Top view 20µm

5 As received Heat treatment: 850 C for 2 h (~8 C /min) then FC. In vacuum until 280 C Microstructure : Comparison

6 20µm As received Heat treatment: 850 C for 2 h (~8 C /min) then FC. In vacuum until 280 C Microstructure : Comparison


Download ppt "Microstructure of the different Ti-6Al-4V Aida Amroussia, PhD Candidate 1 Pr. Carl J Boehlert 1 Dr. Frederique Pellemoine 2 Pr. Wolfgang Mittig 2 1 Michigan."