1. 1. 2. 3. 4. © Durability Of Plain And Blended Cements In Marine Environments Al-Amoudi, OSB THOMAS TELFORD SERVICES LTD, ADVANCES IN CEMENT RESEARCH; pp: 89- 100; Vol: 14 King Fahd University of Petroleum & Minerals http://www.kfupm.edu.sa Summary This study was conducted to investigate the durability of two plain cements (Type I and Type V) and three blended cements prepared with fly ash (FA), silica fume (SF) and blast furnace slag (BFS), in marine environments. Cement paste. mortar and reinforced concrete specimens were exposed to sea water for a period of 2 years. In addition to inspecting the specimens visually, the performance of both plain and blended cements was evaluated by measuring the strength development, reduction in compressive strength, expansion, weight change, reinforcement corrosion and conducting chemical and mineralogical analyses. The visual inspection and compressive strength results indicated that the sulphate attack was somewhat hindered in plain and blended cements despite the high sulphate concentration in the marine environments. The data on reinforcement corrosion confirmed the superior performance of silica fume cement in sea water; followed by blast furnace slag and fly ash cements. The corrosion resistance of Type I cement was marginally better than that of Type V cement. Even though the Cl- concentration and Cl-/OH- ratio in the SF and BFS cements were the highest and much more than the threshold values, the intensity of reinforcement corrosion in these cements was less than that in the plain cements. References: *AM CONCR I, 1995, 31895 ACI *AM PUBL HTLH ASS, 1985, STAND METH EX WAT WA *HIGHW RES BOARD, 1972, 127 HIGHW RES BOARD ALAMOUDI OSB, 1992, ENG GEOL, V33, P111 Copyright: King Fahd University of Petroleum & Minerals; http://www.kfupm.edu.sa

2. 5. 6. 7. 8. 9. 10. 11. 12. 13. 14. 15. 16. 17. 18. 19. 20. 21. 22. 23. 25. 26. 27. 28. 29. 30. 31. 32. 33. 34. 35. 36. 37. 38. 39. 40. 41. 42. 43. 44. 45. 46. 47. 48. © ALAMOUDI OSB, 1992, P 9 INT C CHEM CEM, V5, P438 ALAMOUDI OSB, 1993, CEMENT CONCRETE RES, V23, P139 ALAMOUDI OSB, 1994, CEMENT CONCRETE AGGR, V16, P3 ALAMOUDI OSB, 1994, MAG CONCRETE RES, V46, P113 ALAMOUDI OSB, 1995, ACI MATER J, V92, P236 ALAMOUDI OSB, 1996, ACI MATER J, V93, P191 ALAMOUDI OSB, 1996, CONCRETE SERVICE MAN, P139 ALAMOUDI OSB, 1998, BUILD ENVIRON, V33, P53 ALAMOUDI OSB, 2001, CONCRETE, V35, P45 ALAMOUDI OSB, 2002, IN PRESS CEMENT CONC ALGHAMDI HA, 1986, P INT C CONCR MAR EN, P115 ALGHAMDI HA, 1999, THESIS U ABERDEEN UK ARUP H, 1985, CORR REINF CONC STRU, P151 BROWNE RD, 1979, DEV CONCRETE TECHNOL, P111 BROWNE RD, 1982, DURABILITY BUILDING, V1, P113 CONJEAUD ML, 1980, ACI SP, V65, P39 EGLINTON MS, 1987, CONCRETE ITS CHEM BE FIGG JW, 1979, B I CORROS SCI TECHN, V75, P12 GERWICK BC, 1990, CONCRETE INT AM MAY, P47 24.GJORV OE, 1976, ACI JSEP, P512 GLORY OE, 1971, ACI J P, V68, P60 HARRISON WH, 1990, MAG CONCRETE RES, V42, P113 HAUSMANN DA, 1967, MATERIALS PROTECTION, V6, P19 HOFF GC, 1991, ACI SP, V126, P33 HUSSAIN SE, 1991, THESIS KING FAHD U KALOUSEK GL, 1970, ACI J, P187 LAMBERT P, 1991, MATER STRUCT, V24, P351 LEA FM, 1970, CHEM CEMENT CONCRETE MACPHEE DE, 1993, MAGAZINE CONCRETE RE, V45, P63 MANGAT PS, 1988, CEMENT CONCRETE RES, V18, P44 MASLEHUDDIN M, 1994, ACI SP, V144, P191 MEHTA PK, 1973, CEMENT CONCRETE RES, V3, P1 MEHTA PK, 1975, ASCE J STRUCTURAL DI, V101, P1679 MEHTA PK, 1980, ACI SP, V65, P1 MEHTA PK, 1991, CONCRETE MARINE ENV MINDNESS S, 1981, CONCRETE RASHEEDUZZAFAR, 1989, P 3 INT REP REINF CO, V1, P35 RASHEEDUZZAFAR, 1994, ASCE J MAT CIVIL ENG, V6, P201 REGOURD M, 1980, ACI SP, V65, P63 TUUTI K, 1980, ACI SP, V65 VANAARDT JHP, 1960, P 4 INT S CHEM CEM W, V2, P835 VOGEL AI, 1978, TXB QUANTITATIVE INO WOOD H, 1968, ACI MONOGRAPH, V4 YEGINOBALI A, 1984, P 3 INT C DUR BUILD, V3, P55 Copyright: King Fahd University of Petroleum & Minerals; http://www.kfupm.edu.sa

3. © For pre-prints please write to: abstracts@kfupm.edu.sa Copyright: King Fahd University of Petroleum & Minerals; http://www.kfupm.edu.sa