1. TIG Welding Introduction

2. Outline Background Advantages and Disadvantages Safety
Preparation for TIG Welding
Techniques for Basic Weld Joints
TIG Shielding Gases
Tungsten Electrode Selection
Conclusion
ENBE 499

3. Background What is TIG? Also referred to as GTAW
Tungsten Inert Gas
Also referred to as GTAW
Gas Shielded Tungsten Welding
In TIG welding, a tungsten electrode heats the metal you are welding and gas (most typically Argon) protects the weld from airborne contaminants
ENBE 499

4. Background TIG welding uses a non-consumable tungsten
Filler metal, when required, is added by hand
Shielding gas protects the weld and tungsten
ENBE 499

5. Advantages Welds more metals and metal alloys than any other process
High quality and precision
Pin point control
Aesthetic weld beads
No sparks or spatter
No flux or slag
No smoke or fumes
ENBE 499

6. Disadvantages Lower filler metal deposition rates
Good hand-eye coordination a required skill
Brighter UV rays than other processes
Slower travel speeds than other processes
Equipment costs tend to be higher than other processes
ENBE 499

7. Safety Electric shock can kill.
Always wear dry insulating gloves
Insulate yourself from work and ground
Do not touch live electrical parts
Keep all panels and covers securely in place
Fumes and gases can be hazardous to your health.
Keep your head out of the fumes
Ventilate area, or use breathing device
ENBE 499

8. Safety Welding can cause fire or explosion.
Do not weld near flammable material
Watch for fire; keep extinguisher nearby
Do not locate unit over combustible surfaces
Do not weld on closed containers
Arc rays can burn eyes and skin; Noise can damage hearing.
Wear welding helmet with correct shade of filter
Wear correct eye, ear, and body protection
ENBE 499

9. Preparation for TIG Welding
Preparing the Weld Joint
Many problems are a direct result of using improper methods to prepare the weld joint
One of the most common is the improper use of grinding wheels
Soft materials like aluminum may get embedded with abrasive particles resulting in excessive porosity
Grinding wheels should be cleaned and dedicated only to the material being welded
ENBE 499

10. Preparation for TIG Welding
Preparing Aluminum for Welding
Very susceptible to contaminants
Surface oxide must be removed
Special abrasive wheels are available for aluminum
Stainless steel wire brushes recommended
Both sides of the joint should be cleaned if it contains foreign material
ENBE 499

11. Techniques for Basic Weld Joints
Arc Length
Arc length normally one electrode diameter, when AC welding with a balled end electrode
When DC welding with a pointed electrode, arc length may be much less than electrode diameter
ENBE 499
*Figure copied from “TIG Handbook”

12. Techniques for Basic Weld Joints
Gas Cup Size
Inside diameter of gas cup should be at least three times the tungsten diameter to provide adequate shielding gas coverage
Picture on right shows example of gas cup size and torch position
1-Workpiece, 2-Work clamp, 3-Torch, 4-Filler rod, 5-Gas cup, 6-Tungsten electrode
ENBE 499
*Figure copied from “TIG Handbook”

13. Techniques for Basic Weld Joints
Arc Starting with High Frequency
Torch position on left shows recommended method of starting the arc with high frequency when the torch is held manually
By resting gas cup on base metal there is little danger of touching the electrode to the work
After arc is initiated, torch can be raised to proper welding angle
ENBE 499
*Figure copied from “TIG Handbook”

14. Techniques for Basic Weld Joints
Manual Torch Movement
ENBE 499
*Figure copied from “TIG Handbook”

15. Techniques for Basic Weld Joints
Manual Torch Movement
Torch and filler rod must be moved progressively and smoothly so the weld pool, the hot filler rod end, and the solidifying weld are not exposed to air that will contaminate the weld metal area or heat affected zone
When arc is turned off, post flow of shielding gas should shield the weld pool, electrode, and hot end of the filler rod
ENBE 499

16. Techniques for Basic Weld Joints
Butt Weld and Stringer Bead
Be sure to center weld pool on adjoining edges
When finishing a butt weld, torch angle may be decreased to aid in filling the crater
Torch and rod position for welding the butt weld and stringer bead
ENBE 499
*Figure copied from “TIG Handbook”

17. Techniques for Basic Weld Joints
Lap Joint
Pool is formed so that the edge of the overlapping piece and the flat surface of the second piece flow together
Torch angle is important because the edge will become molten before the flat surface
Enough filler metal must be added to fill the joint as illustrated on the right
Torch and rod position for welding the lap joint
ENBE 499
*Figure copied from “TIG Handbook”

18. Techniques for Basic Weld Joints
T-Joint
Edge will heat up and melt sooner
Torch angle illustrated will direct more heat onto the flat surface
Electrode may need to be extended further beyond the cup in order to hold a short arc
Torch and rod position for welding the T-joint
ENBE 499
*Figure copied from “TIG Handbook”

19. Techniques for Basic Weld Joints
Corner Joint
Both edges of the adjoining pieces should be melted and the pool kept on the joint centerline
Sufficient filler metal is necessary to create a convex bead as shown
Torch and rod position for welding the corner joint
ENBE 499
*Figure copied from “TIG Handbook”

20. TIG Shielding Gases
Argon
Helium
ENBE 499

21. TIG Shielding Gases Helium Argon Good arc starting
Good cleaning action
Good arc stability
Focused arc cone
Lower arc voltages
10-30 CFH flow rates
Helium
Faster travel speeds
Increased penetration
Difficult arc starting
Less cleaning action
Less low amp stability
Flared arc cone
Higher arc voltages
Higher flow rates (2x)
Higher cost than argon
ENBE 499

22. Conclusion
TIG welding is an exciting skill that proves itself useful in countless applications
Because it welds more metal and metal alloys than any other process, TIG welding should be regarded as an important tool where experience is the teacher
Welding parameters and tungsten electrode selection tables are recommended values and should be used as a guideline
Information presented here is only the tip of the iceberg, and further research and hands-on involvement should be pursued to be comprehensive
ENBE 499

23. THANK U
ENBE 499