From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
Aqueous concentration of aluminum ions at different pH values for fluoride-treated and untreated reference: (a) at pH 4, 6, 9 and (b) at pH 2, 12

2. Date of download: 11/5/2017
Copyright © ASME. All rights reserved.
From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
SEM micrograph of (a) untreated alumina and (b) fluoride-treated alumina

3. Date of download: 11/5/2017
Copyright © ASME. All rights reserved.
From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
EDS spectrum of fluoride-treated alumina

4. Date of download: 11/5/2017
Copyright © ASME. All rights reserved.
From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
Concentration of aluminum ions as a function of fluoride concentration in aqueous solution at pH 6.0, 1 g alumina in 30 ml potassium fluoride solution for 24 h

5. Date of download: 11/5/2017
Copyright © ASME. All rights reserved.
From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
Comparison of aqueous concentrations of aluminum ions at different pH values, comparison of different salts for fluoride-treated and untreated reference

6. Date of download: 11/5/2017
Copyright © ASME. All rights reserved.
From: Resistance Improvement of Aluminum Surface to Corrosion Through Reactions With Fluoride Ions
ASME J of Nuclear Rad Sci. 2017;3(3): doi: /
Figure Legend:
Picture of aluminum stripes: (a) “fluoride-treated” and (b) untreated reference