1. Double-sided YBCO thin films

2. Cleanroom for deposition

3. Measured with inductive coil with 5 mm in diameter
Homogeneous Tc distribution
Measured with inductive coil with 5 mm in diameter

4. By Michele Lorenz

5. JC = 2.5 ~ 2.9 MA/cm2 Homogeneous Jc distribution Measured with
Leipzig
jc-scan system
JC = 2.5 ~ 2.9 MA/cm2

6. Rs distribution
Measured at 145GHz, 75K,
by FZK, Germany
0.24－0.37 mW converted to 10GHz

7. XRD results of 3 inch sample
edge
center

8. Surface structure of YBCO films
AFM images, the heights of the designated steps are given: A-B,1.136nm; B-C, 1.172nm; C-D, 1.131nm; E-F, nm; F-G, 1.142nm; G-H,1.164nm.

9. The typical properties of 500 nm films are as follows:
MTI Corporation Lead suppler for Advanced Materials and Lab Equipment
We can provide 2 to 3 inch YBCO double-sided YBCO thin films in a small batch (e.g pieces) in one month after substrate delivered.
The typical properties of 500 nm films are as follows:
Tc ~ 90K, Delta Tc less than 1K
Jc77K,0T ~2-3 MA/cm2
Rs77k,10GHz~ mohm