I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev Institute of Hydrodynamics SB RAS
2
1. Motivation 2. Structure of Al-Ti composite produced by explosive welding 3. Peculiarities of Al 3 Ti layer formation during annealing 4. Some results of mechanical tests 5. Conclusion
3
High specific stiffness High heat resistance Low density Good results in fatigue and impact tests Combining the properties of both the hard and refractory intermetallics and the ductile matrix Dilution of titanium with cheaper aluminum reduces the cost of material
7
Upper part of compositelower part of composite
9
Al distribution Ti distribution
11
1 hour5 hours100 hours Wavy interfaces plane interfaces
12
5 hours annealing 100 hours annealing
14
630 o C annealing, 30 min
18
Al 3 Ti
19
Near Al Middle of the Al 3 Ti layerNear Ti Al Al3Ti Ti
20
Dark field OMBtight field OM Btight field OM, Iron-rich precipitation in the Al-layer
21
Al –Al 3 Ti – Ti Al – Ti Al 3 TiTi
24
Explosive welding of Ti and Al plates with subsequent annealing is effective technological process for MIL composites production. Titanium trialuminide (Al 3 Ti) is the only intermetallic compound between Al and Ti formed under annealing. The most favorable place for Al 3 Ti growth are former vortexes The best intermetallic structure is on the Ti-Al 3 Ti boundary. On Al-Al 3 Ti boundary pores and microcracks were found One of the most important goals arisen during explosive welding and annealing is addressing the causes of residual stresses, pores and microcracks formation