4. Plasma Cutting and Its Effect on Mild Steel Brad RushMynda SongerEliot Speed

5. Background of Plasma Arc Process In 1941 the U.S. defense industry was looking for a way to join light metals, from this came Tungsten Inert Gas (TIG) welding In 1941 the U.S. defense industry was looking for a way to join light metals, from this came Tungsten Inert Gas (TIG) welding It was found that by passing a gas through the TIG arc that metal could be cut by gas in a plasma state It was found that by passing a gas through the TIG arc that metal could be cut by gas in a plasma state TIG and plasma arc processes were created for the aerospace industry, primarily for aluminum which is difficult to weld by other processes and difficult to cut with a torch TIG and plasma arc processes were created for the aerospace industry, primarily for aluminum which is difficult to weld by other processes and difficult to cut with a torch CNC Plasma Cutting Machine, 1980

6. How a Plasma Cutter Works An arc is used to ionize the gas around a high voltage arc An arc is used to ionize the gas around a high voltage arc This ionized gas is superheated by the arc to plasma This ionized gas is superheated by the arc to plasma In the plasma state, the gas is at 30,000˚F, reducing the steel to a molten state, allowing the stream of gas to push it out of the cut In the plasma state, the gas is at 30,000˚F, reducing the steel to a molten state, allowing the stream of gas to push it out of the cut

7. Effect of Plasma Cutting at Different Amperages We examined the microstructure of ¼ thick 1018 mild steel that was cut at different amperages We examined the microstructure of ¼ thick 1018 mild steel that was cut at different amperages The steel was cut at 15, 22.5, and 30 amps The steel was cut at 15, 22.5, and 30 amps The three samples were mounted and polished, and the microstructures were examined and photographed The three samples were mounted and polished, and the microstructures were examined and photographed

8. 15 Amp Cut This amperage was too low for the thickness of steel, so the cut that was made was slowThis amperage was too low for the thickness of steel, so the cut that was made was slow The sample was heated to around 1200˚F, annealing the steel in the heat affected zone (HAZ)The sample was heated to around 1200˚F, annealing the steel in the heat affected zone (HAZ) The annealed steel can be seen by the lighter region in the HAZ and near the edge of the steel, which is ferrite and pearliteThe annealed steel can be seen by the lighter region in the HAZ and near the edge of the steel, which is ferrite and pearlite Heat Affected Zone Border Edge of Steel

9. 22.5 Amp Cut The amperage was correct for this cut, so the annealed region, or HAZ, was very small due to the cut being the correct speed and heatThe amperage was correct for this cut, so the annealed region, or HAZ, was very small due to the cut being the correct speed and heat Only the edge was heated to around 1200˚F as seen in the photographOnly the edge was heated to around 1200˚F as seen in the photograph The dark region is ferrite and martensite due to the austenization and slow cooling, while the light region is ferrite and pearlite, since it is unaffected by the cutThe dark region is ferrite and martensite due to the austenization and slow cooling, while the light region is ferrite and pearlite, since it is unaffected by the cut EdgeHAZ Border

10. 30 Amp Cut The amperage for this cut was too high and created a larger HAZ, even though the speed of the cut was greaterThe amperage for this cut was too high and created a larger HAZ, even though the speed of the cut was greater The edge and some of the interior was all heated to around 1200˚FThe edge and some of the interior was all heated to around 1200˚F The HAZ contains ferrite and martensite due to austenization as in the 22.5 amp cut, as in the 22.5 amp cut the ferrite and pearlite region is the unaffected regionThe HAZ contains ferrite and martensite due to austenization as in the 22.5 amp cut, as in the 22.5 amp cut the ferrite and pearlite region is the unaffected region HAZ Border Edge

11. Conclusion At 22.5 amps, the steel has the smallest HAZ, as this is the correct amperage to cut ¼ mild steel At 22.5 amps, the steel has the smallest HAZ, as this is the correct amperage to cut ¼ mild steel The plasma cutter can cut steel about 10 times faster than a reciprocating saw The plasma cutter can cut steel about 10 times faster than a reciprocating saw Best cutting tool for light metals, especially as an alternative to an oxy-acetylene torch Best cutting tool for light metals, especially as an alternative to an oxy-acetylene torch