1. Electrochemical Performance of LiFePO4 Batteries made with Carbon Nanofibers Hamzah Khan San Francisco State University
introduction
Results
Methods
results
Discharge Profile:
Cyclability:
conclusion
No discharge capacity improvement at 0.1C
Excellent rate performance at extremely high C- Rate
Improved Cyclability at 5C
C-Rate Performance:
Methods
Future work
Fabrication Process:
Slurry making
Coating
Cutting cathode
Assembly
Testing
Data Analysis
Fabricate more batteries to verify observations
Perform Cyclic Voltammetry Measurement
Start looking into modeling our experimental results
Acknowledgements
Financial support from the REU Site in Physics at Howard University NSF Award PHY is gratefully acknowledged
Dr. Quinton Williams
Adewale Adepoju