Download presentation
Presentation is loading. Please wait.
Published byMaddison St. george Modified over 9 years ago
1
Reduction of Magnesium Oxide Brian Peterson Solar Thermochemical Ammonia: A More Sustainable Way to Feed the World Mg Nitride +CO ← Mg Oxide + C +N 2 Mg Nitride + H 2 O → Mg Oxide + NH 3 N2N2 C (Biomass/Charcoal) CO NH 3. H2OH2O Ca Nitride ← “Ca solids” + N 2 N2N2 NH 3. H2H2 Ca Nitride + H 2 → “Ca solids”+ NH 3 Introduction Corrosion of Calcium Nitride Ammonia is critical as a source of fixed nitrogen as fertilizer for agriculture globally. It has been estimated that between one third and one half of the world’s population could not be sustained without chemical processes that synthetically produce ammonia from nitrogen in the air. The current standard for ammonia production is the Haber-Bosch process. This 100-year-old process consumes large quantities of fossil fuels and requires large amounts of energy (accounts for nearly 2% of energy usage globally). It is imperative to study alternative, sustainable processes to feed both the growing world population and the growing biofuel industry. Comparison ProcessHaber-BoschSolar Ammonia Pressure300 bar1 bar Temperature500 °C400-1200 °C Energy SourceNatural GasSolar Energy Hydrogen SourceNatural GasWater or H 3 ReactionCatalystNo Catalyst Tasks In general, the Solar Ammonia process utilizes a metal nitride which is corroded with a hydrogen source (either H 2 or H 2 O). When water is used, the metal nitride corrodes very easily at room temperature and atmospheric pressure, but a rather unreactive metal oxide is formed. The more difficult step is recycling the metal oxide because it requires much higher temperatures and a reducing agent such as carbon. 1,2,3 Brian Peterson, 2 Ronny Michalsky, 2 Peter Pfromm 1 NSF REU Program, 2 Kansas State University Center for Sustainable Energy 3 Missouri University of Science and Technology Department of Chemical Engineering Reduction of Magnesium Oxide Test effects of the addition of Iron(III) Oxide and Chromium(III) Oxide at 1200 °C Analyze kinetics of best case mixtures Corrosion of Calcium Nitride Identify composition of solids after reaction Analyze the kinetics at various H 2 flow rates Methods Make different molar combinations of 3 solid reactants React Nitrogen using Solar Concentrator and reactor. Gather data on kinetics of 3 mixtures, one with Iron(III) Oxide added, one with Chromium (III) Oxide added, and a reference without additional oxides. Run using an indoor furnace and reactor Results and Conclusions Goal Reduce Magnesium Oxide into the form of Magnesium Metal or Magnesium Nitride Fig1 : Yield of 8 mixtures using Solar Concentrator Conclusions from Figure 1: Higher ratios of Carbon to Magnesium Oxide heavily influence Magnesium Nitride Chromium(III) Oxide appears to have a stronger influence than Iron(III) Nitride on the production of Magnesium Nitride Molar RatioMass % Mg Lost MgO:C:FeO3:Cr2O330 min.60 min.120 min. 1:8:0:049.21%50.55%-43.35% 1:8:1:0-60.80%-74.01%-154.78% 1:8:0:17.09%-24.82%44.06% Tab1 : Percent of Magnesium atoms that left the system at different reaction times which correlates to Magnesium reduced. Conclusions from Table 1: Heavy error exists, most likely in the X-Ray Diffraction analysis of solid composition Better analytical techniques might be considered Methods React Calcium Nitride with H 2 at various temperatures using an indoor reactor and determine the composition of the solids Gather kinetics data for the reaction at 700°C Fig2 : Mol percent of Nitrogen atoms that left the system, presumably as Ammonia at different reaction temperatures Fig3 : Mass percent of Calcium Hydride in the solid phase after reactions at various temperatures Fig4 : Mol percent of Nitrogen atoms liberated, likely as Ammonia at different Hydrogen flows Conclusions from Figure 2: As expected, more Ammonia is produced (Nitrogen liberated) at higher temperatures, but levels off after 700 °C Flow rate experiments (Figure 4) should be performed at 700 °C Conclusions from Figure 3: More Calcium Hydride is produced at higher temperatures Also Calcium Hydride is vaporized at the higher temperatures and exits the system Conclusions from Figure 4: Hydrogen flow rate has little effect on Ammonia formation Thus this is likely a diffusion limited reaction Results and Conclusions Goal Maximize the production of Ammonia Solar Concentrator
Similar presentations
© 2024 SlidePlayer.com. Inc.
All rights reserved.