The Metallurgy of Welding; Welding Design and Process Selection
CHAPTER 7-3
2
Fusion Weld Zone Figure Characteristics of a typical fusion weld zone in oxyfuel gas and arc welding. See also Figs and
3
Grain Structure in Shallow and Deep Welds
(b) Figure Grain structure in (a) a deep weld (b) a shallow weld. Note that the grains in the solidified weld metal are perpendicular to the surface of the base metal. In a good weld, the solidification line at the center in the deep weld shown in (a) has grain migration, which develops uniform strength in the weld bead.
4
Incomplete Fusion Figure Low-quality weld beads, the result of incomplete fusion. Source: American Welding Society.
5
Discontinuities in Fusion Welds
Figure Schematic illustration of various discontinuities in fusion welds. Source: American Welding Society.
6
Cracks in Welded Joints
Figure Types of cracks (in welded joints) caused by thermal stresses that develop during solidification and contraction of the weld bead and the surrounding structure. (a) Crater cracks. (b) Various types of cracks in butt and T joints.
7
Distortion After Welding
Figure Distortion of parts after welding: (a) butt joints; (b) fillet welds. Distortion is caused by differential thermal expansion and contraction of different parts of the welded assembly.
8
Residual Stresses Developed During Welding
Figure Residual stresses developed during welding of a butt joint. Source: American Welding Society.
9
Overview of Commercial Joining Processes
10
Overview of Commercial Joining Processes (cont.)
11
Overview of Commercial Joining Processes (cont.)
12
Destructive Techniques
Figure Two types of specimens for tension-shear testing of welded joints. Figure (a) Wrap-around bend test method. (b) Three-point bending of welded specimens--see also Fig
13
Testing of Spot Welds Figure (a) Tension-shear test for spot welds. (b) Cross-tension test. (c) Twist test. (d) Peel test; see also Fig
14
Welding Design Guidelines
Figure Design guidelines for welding. Source: J. G. Bralla (ed.), Handbook of Product Design for Manufacturing. Copyright ©1986, McGraw-Hill Publishing Company. Used with permission.
15
Standard Identification and Symbols for Welds
Figure 29.16
16
Weld Design Selection Figure 29.17